BALINIT® TRITON STAR combines a high hardness with an extremely low coefficient of friction. Being a diamond-like carbon coating (DLC), it provides particularly good protection against abrasive and adhesive wear. The added metal-based support layer (chromium nitride) significantly increases the load-bearing capacity and makes BALINIT® TRITON STAR the coating of choice e.g. for a wide range of popular aluminium forming processes.
| BALINIT TRITON STAR | |
|---|---|
| Coating material | CrN / a-C:H |
| Coating technology | PACVD |
| Coating colour | black |
| Coating hardness HIT [GPa]* | ~15-25 |
| Coefficient of friction (dry) vs. steel** | 0.1 - 0.2 |
| Max. service temp. [°C]**** | 300 |
| Process temperature [°C] | < 250 |
| General remark | All given data are approximate values, they depend on application, environment and test condition. |
| *Coating hardness HIT [GPa] | Measured by nano indentation according to ISO 14577. For multilayers the hardness of the different layers varies. Hardness can be adapted to the application. |
| **Coefficient of friction (dry) vs. steel | Determined by ball-on-disc test in dry condition with an Steel ball according to ASTM G99. During run-in the given values may be exceeded. |
| ****Max. service temp. [°C] | These are approximate values out of the field. Due to thermodynamic laws there is a dependency of pressure in application. |